Abstract
Abstract Durability of a nickel and scandia-stabilized zirconia cermet anode against toluene in hydrogen was evaluated in this paper. Anode deterioration was judged by the loss of elemental nickel from a surface of an anode. Elemental nickel loss was observed when the toluene concentration was 3 or 10 g/Nm3, steam to carbon ratio was 1, and current density was 0.5 A/cm2 at both temperatures: 1073 K and 1173 K. Therefore the tolerance criterion must be less than 3 g/Nm3 in hydrogen in the experimental conditions. However, the deterioration can be mitigated to some extent by increasing the operating temperature, steam-to-carbon ratio, or current density. Anode deterioration was also mitigated when hydrogen concentration in the fuel gas was nearly identical to that of wood gas. The influence of hydrogen concentration in the fuel gas on deterioration may be substantial. The loss of elemental nickel could not be detected instantaneously by electrochemical diagnosis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.