A TGA-FTIR study on the effect of CaCO 3 on the thermal degradation of EBA copolymer

Abstract

The thermal degradation of ethylene–butyl acrylate (EBA) copolymer with/without CaCO 3 has been studied via the combined TGA-FTIR technique at a heating rate of 10 °C/min in high purified N 2. The volatiles from EBA on heating include mainly 1-alkene (i.e. 1-butene), hydrocarbon chain fragments, CO 2, butyl acrylate-containing fragment, as well as the trace of CO and H 2O in the temperature range of 350–500 °C. The 1-butene is most likely formed through ester pyrolysis. The two bands at 2925 cm −1 (asymmetric stretching of –CH 2 –, corresponding to hydrocarbon chain fragments), and 720 cm −1 (plane rocking of –CH 2–, representative of the alkanes with low molecular weight –(CH 2) n –, n ≥ 4) were indicative of the hydrocarbon species essentially accompanied with acrylate-containing fragments at high temperature. Based on the data message of the TGA and the Gram–Schmidt curves, it shows that the EBA copolymer becomes much more stable in the presence of CaCO 3. The volatiles involved in the pyrolysis of EBA copolymer have qualitatively chemical composition similar to the case with CaCO 3. Obviously, both the descending flammable volatiles and the ascending creation in CO 2 from EBA copolymer do come intimately from the interposition of CaCO 3. That both the prolonged ignition time and the reduced heat release rate of EBA during combustion depend, therefore, on the presence of CaCO 3 is being expected.