A Systematic Investigation on the Effect of Carbon Nanotubes and Carbon Black on the Mechanical and Flame Retardancy Properties of Polyolefin Blends.

Abstract

Listen

Translate article

Due to high filler loading, clean, commercial, thermoplastic, flame-retardant materials are mechanically unstable when insulating wires and cables. In this study, composite formulations of linear low-density polyethylene (LLDPE)/ethylene-vinyl acetate (EVA) containing a flame retardant, such as magnesium hydroxide (MH; formula: Mg(OH)2) and huntite hydromagnesite (HH; formula: Mg3Ca(CO3)4, Mg5(CO3)4(OH)2·3H2O), were prepared. The influence of carbon nanotubes (CNTs) and carbon black (CB) on the mechanical properties and flame retardancy of LLDPE/EVA was studied. Three types of CNTs were examined for their compatibility with other materials in clean thermoplastic flame-retardant compositions. The CNTs had the following diameters: 10-15 nm, 40-60 nm, and 60-80 nm. Optimum mechanical flame retardancy and electrical properties were achieved by adding CNTs with an outer diameter of 40-60 nm and a length of fewer than 20 nm. Large-sized CNTs result in poor mechanical characteristics, while smaller-sized CNTs improve the mechanical properties of the composites. CB enhances flame retardancy but deteriorates mechanical properties, particularly elongation at break, in clean, black, thermoplastic, flame-retardant compositions. Obtaining satisfactory compositions that meet both properties, especially formulations passing the V-0 of the UL 94 test with a minimum tensile strength of 9.5 MPa and an elongation at break of 125%, is challenging. When LLDPE was partially substituted with EVA, the limiting oxygen index (LOI) increased. The amount of filler in the formulations determined how it affected flammability. This study also included a reliable method for producing clean, black, thermoplastic, flame-retardant insulating material for wire and cable without sacrificing mechanical properties.