Abstract
Abstract Remarkable progress has been made in perovskite solar cells (PSCs) recently. However, the defects present in the perovskite layer act as non-radiative recombination centers to decrease the stability and restrict the further performance improvement of the device. We report herein a sulfur-rich two-dimensional small molecule, SMe-TATPyr, as a bifunctional layer to efficiently passivate the surface defects of perovskite and facilitate the hole transfer at the perovskite/spiro-OMeTAD interface. X-ray photoelectron spectroscopy analyses show that the sulfur atoms of SMe-TATPyr can passivate the uncoordinated Pb2+ defects and suppress the Pb0 defect formation as Lewis bases. As a result, the power conversion efficiency of PSCs is distinctly increased from 20.4% to 22.3%. Moreover, this simple interfacial modification could effectively enhance the stability of unencapsulated PSCs to retain 95% of the initial efficiency after storage for 1500 h at ambient conditions, in contrast to 70% efficiency retention of the device without SMe-TATPyr under the same conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.