Abstract
7A52 Al alloy plates was welded using twin-wire metal inert gas arc welding (TMW) .Stress corrosion cracking (SCC)behavior of the parent material and the welded specimens was investigated by the slow strain rate tensile(SSRT)test method respectively. Electrochemical impedance spectroscopy (EIS) was conducted to understand electrochemical corrosion behavior of 7A52 Al alloy and its TMW weldment. It was found that the welded specimens exhibited higher SCC susceptibility than the parent materials under SSRT testing in seawater. The EIS result showed that the weld zone exhibited higher corrosion resistance than that of the parent material. Hydrogen embrittlement is a crucial factor that leads to the failure of the welded specimens during SSRT test in seawater.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.