Abstract
The traditional preparation process of natural rubber latex requires tedious treatment of a variety of rubber additives. In this paper, a new process of wet mixed grinding was used to prepare a reinforced vulcanization mixture and a rapid vulcanization effect. The effect of different amounts of vulcanization mixtures on the mechanical properties of natural latex film was studied, and the pre-vulcanization process of latex and the vulcanization process of film were optimized. The results showed that with the increase in the amount of vulcanization mixture, the tensile strength increased from 5.96 MPa to 29.28 MPa, and the tear strength increased from 7.59 kN/m to 52.81 kN/m. When the vulcanization temperature of the latex film is heated from 80 °C to 100 °C, the vulcanization time is shortened by 5~6 times. The new vulcanization mixture prepared in this work has the characteristics of simple production and fast vulcanization speed, which provides a new solution for the development of the latex product industry.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.