Abstract
We studied the physical properties of <TEX>$Co_3$</TEX><TEX>$O_4$</TEX>-added Ni-Zn ferrite which were sintered at 1050~110<TEX>$0^{\circ}C$</TEX> for 2 hours. X-ray diffraction showed a spinel structure, and optical microscopy showed grain sizes of 5 to 10 <TEX>$\mu\textrm{m}$</TEX>. As the sintering temperature was increased from <TEX>$1050^{\circ}C$</TEX> to <TEX>$1070^{\circ}C$</TEX>, the initial permeability and magnetic induction increased, and both of the loss factor and the coercive force decreased. The Curie temperatures were about <TEX>$^234~245{\circ}C$</TEX> with added <TEX>$Co_3$</TEX><TEX>$O_4$</TEX>. The initial permeability was 350 to 420 and maximum magnetic induction density and coercive force 4870G to 4980G and 0.15 Oe to 0.21 Oe, respectively which were similar to those of Ni-Zn ferrite synthesized in the conventional process. The frequency of specimen was in the range of 1MHz to 300MHz. In the plot of initial permeability vs. frequencies, a <TEX>$180^{\circ}C$</TEX> rotation of the magnetic domain could be perceived in a broad band of microwave before and after the resonance frequency.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.