Abstract
This paper investigates the effects of graphite added as a conditioner, of Lantanum containing nodulariser and of pouring temperature on the formation of shrinkage porosity in ductile iron casting with an eutectic composition. In this experiment for each heat the cooling curves were recorded by the use of Quick-Cups (thermal analysis cups) and different solidification parameters such as TElow, GRF1, GRF2 and TS were calculated and compared with the porosity which was found from the microstructure examination. The results show that there is a good correlation between the amount of the shrinkage formation and the thermal analysis values. Also this experiment confirm that by using certain treating elements and pouring temperature which was between 1340-1350°C it is possible to eliminate the shrinkage defects in ductile iron castings without using feeders.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.