Abstract

Biomimetic growth of calcium phosphate over natural polymer may be an effective approach to constituting an organic/inorganic composite scaffold for bone tissue engineering. In this work, N-methylene phosphochitosan (NMPCS) was prepared via formaldehyde addition and condensation with phosphoric acid in a step that allowed homogeneous modification without obvious deterioration in chitosan (CS) properties. The NMPCS obtained was characterized by using FT-IR and elemental analysis. The macroporous scaffolds were fabricated through a freeze-drying technique. A comparative study on NMPCS and CS scaffold biomimetic mineralization was carried out in different media, i.e, a simulated body fluid (SBF) or alternative CaCl(2) and Na(2)HPO(4) solutions respectively. Apatite formation within NMPCS and CS scaffolds was identified with FT-IR, scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) and X-ray diffractometery (XRD). The results revealed alternate soaking of the scaffolds in CaCl(2) and Na(2)HPO(4) solutions was better than soaking in SBF solution alone in relation to apatite deposition on the scaffold pore walls. Biomineralization provides an approach to improve nature derived materials, e.g., chitosan derivative NMPCS properties e.g., compressive modulus, etc. SEM image of a NMPCS/apatite composite scaffold.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.