Abstract
In this article, the pre-oxidized fiber felt composite material was firstly prepared by a mold press process, and the pre-oxidized fiber and resin were used as the reinforcing material and substrate of composite material, respectively. The pretreatment method of the pre-oxidized fiber felt and the impact of the amount of curing agent and the curing pressure on the mechanical properties of the composite material were studied, and the tensile and flexural properties were assessed to optimize the preparation process of composite material. Results show that when the curing agent accounts for 60% of the epoxy resin and the curing pressure is 3 MPa, the best tensile and flexural properties of the prepared composite material are achieved. The mechanical properties for the pretreated composite sheet prepared from pre-oxidized fiber were superior to those for the untreated sheet.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.