Abstract
Thin films of sodium salicylate were deposited by spin coating from a solution prepared by dissolving sodium salicylate in methanol. The films were characterized by X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, UV–visible spectroscopy and spectrofluorometry. The films were crystalline with a strong blue fluorescence peak at an emission wavelength of 419.3 nm. The influence of solution concentration, spin speed and annealing temperature on the fluorescence intensity was studied. Optimum results were obtained with a solution whose concentration was 2.5 M. It was found that lower spin speed resulted in higher fluorescence intensity. Moreover, the fluorescence intensity decreased as the annealing temperature was increased. The durability of the films over a period of 30 days was also investigated, and films annealed at higher temperatures were found to be less degraded with time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.