Abstract
Cellulose acetate (CA) nanofibers were electrospun in trifluoroacetic acid (TFA) under various conditions of concentration, voltage and dope flow rate while tip to collector distance (TCD) kept constant. Results showed that concentrations lower than 8 wt. % could only be electrospun at low flow rates. Bead free fibers were easily electrospun from higher CA concentrations 13 wt. % to 15 wt. %. Concentrations greater than 15 wt. % formed a viscous solution that could not be uniformly dispersed, thus impeding electrospinning. Medium voltage 20KV was found to produce good fibers while flow rates of 0.5ml/h and above, produced non-uniform fibers with a wide range. Average fiber diameters of 104nm and 129nm were formed at 13 wt. % and 15 wt. % (0.4ml/h, 20KV) respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.