Abstract
Cr1-xAlxN/CrN/Cr multilayer films with a range of different Al contents were deposited on 9–12% Cr heat-resistant steel using direct current magnetron sputtering (DCMS). The chemical composition, roughness, cross-sectional structure, oxidation resistance and kinetic model of oxidation of the resulting films were investigated using various techniques. We discovered that Al atoms substituted for Cr atoms, while the crystal structure remained unchanged. Since Al doping decreases the lattice constants and hinders grain growth, the roughness of the film decreases, and the microstructure becomes denser, which is beneficial to the enhancement of oxidation resistance. According to the kinetic model, internal diffusion is the main restrictive step in this process. Increasing the Al content aids in the formation of an amorphous oxide surface layer that is abundant in Al. When the Al content is sufficiently high, the diffusion of oxygen into the 9–12% Cr steel substrates is prevented by the oxide surface layer of the film, which protects the substrates from further oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.