Abstract
A novel method was developed for the synthesis of titanate nanosheets with high surface area. A solid-state mixture of NaOH and TiO 2 was reacted at 600 °C for several minutes. The aqueous dispersion of the resulting melt was aged at room temperature for periods up to 14 days. After hydrochloric acid treatment and washing procedures, the reaction product was characterized by X-ray diffraction, Raman spectroscopy, N 2-sorption and small-angle X-ray scattering measurements. The titanate compound not subjected to the aging process was amorphous and possessed a microporous framework, while the aged samples displayed nanosheet morphology and high specific surface area (396–509 m 2 g −1). It was revealed that the very short heat treatment is of crucial importance for the titania-titanate phase transformation, while the aging process is needed for the morphological evolution of the titanate samples. The effects of the aging time on the structure and the morphology are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.