A review of the effect of a/W ratio on fracture toughness (II) —experimental investigation in LEFM

Abstract

Many experimental investigations have previously been performed and recently done on different shipbuilding structural steels where the specimens size and crack depth/specimen width (a/W) were varied. A series of interesting results have been gained. It is worthwhile to have a review on the effect of a/W ratio on fracture toughness, and further theoretical analysis is necessary. In this paper, experimental work in elasticplastic fracture mechanics (EPFM) was discussed. Tests had been carried out on 10 kinds of strength steels. Results showed that Ji and δ1 values increased with decreasing a/W when a/W 0.3, the toughness was found to be independent of a/W. Slip line field analysis shows that for shallow cracks, the hydrostatic stress is lower than that from standard deeply cracked bend specimen which develops a high level of crack tip constraint, provides a lower bound estimate of toughness, and will ensure an unduly conservative approach when applied to structure defects especially if initiation values of COD/J-integral are used.