Abstract
Two kinds of commercial LED phosphors (green phosphor LuAG:Ce3+ and red phosphor CaAlSiN3:Eu2+) with polymethyl methacrylate (PMMA) powders were mixed to prepare film phosphors with tunable emission peak in photoluminescence spectrum by flat vulcanizing machine under the temperature of 170 oC and pressure of 2 MPa. The physical phase, surface morphology, transmittance, luminescence spectra of samples were characterized by means of X-ray diffraction (XRD), Environmental scanning electron microscopy (ESEM), Ultraviolet-Visible (UV-Vis) spectrophotometry and Fluorescence spectrometer. The results show that the film phosphors phase was consistent with raw phosphors, phosphor particles were uniformly distributed, and fluorescence spectra with different proportions of phosphors in different position can be adjusted. Tested by HSP 3000 spectrum analyzer, the white LEDs fabricated by blue chip and composite film phosphor containing 5 wt% green phosphor and 1.5 wt.% red phosphor, which refers to the remote excitation technique, possessed color coordinate of (0.3715, 0.3280) and color rendering index (CRI) of 87 when it was driven at power of 36 V/140 mA, reaching the international advanced level.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.