Abstract

Neutron diffraction and finite element method were combined to analyze the through-thickness residual stresses in the thick weld plate considering back chipping. Large residual stresses were generated near the surface. Furthermore, the effect of back chipping width, the heat input of the back weld after back chipping, interpass temperature and plate thickness on the residual stresses were conducted by finite element method. The results showed that larger back chipping width could be helpful to decrease the risk of stress corrosion crack. With the decrease of heat input, the stress variation becomes more obvious. The interpass temperature has an obvious effect on the longitudinal residual stresses but little effect on the transverse residual stresses. Nevertheless, the plate thickness has little influence on the residual stress distribution law. Based on the finite element method results, a formula focused on the 10-40 mm thick plates was fitted to calculate residual stresses with the change of depth through thickness, which was verified by neutron diffraction measurement.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.