Abstract
ABSTRACTThis paper reports the Metal Organic Chemical Vapor Deposition (MOCVD) growth of GaN nanostructures. The use of MOCVD allows the direct integration of these nanostructures into pre-existing device technology. The formation of GaN nanostructures grown on AlN epitaxial layers were studied as a function of growth temperature, growth rate, V-III ratio and the amount of deposited material. A wide range of temperatures from 800 °C to 1100 °C and V-III ratios from 30 to 3500 were applied to determine the optimal growth conditions for nucleation studies in a modified production reactor. Small GaN nanostructures with lateral dimensions below 50 nm and low aspect ratios were obtained using relatively low temperatures of 815 °C and extreme metal-rich growth conditions. Island densities up to 1010cm−2were achieved using silane as an anti-surfactant to increase the available nucleation sites. Manganese has been incorporated into these nanostructures to enhance the multifunctional ferromagnetic properties of GaMnN.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.