Abstract
Due to simultaneous synthesis of WC and W 2C phases in most of the synthesis processes and lower mechanical properties of W 2C than WC, in this work the possibility of production of nano-crystalline WC single phase as a useful refractory ceramic by means of mechanical alloying has been investigated. The raw materials containing W and C with WC were milled in a planetary ball mill. The sampling has been done in different times. As it was expected, XRD studies showed that after 75 h of milling the WC with W 2C were produced. By adding WC to the raw materials in the beginning of the process it led to the fact that after 50 h of milling WC was synthesized only without any other phases which remained stable at the higher times while milling. During broadening of XRD peaks, the size of synthesized crystalline WC was estimated in the order of nano-meter. Crystalline size and mean strain of synthesized WC in the system without additive were higher and lower than the system containing WC, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have