Abstract
Due to the decomposition temperature of Polyamide 66 (PA66) in the environment is close to its thermoforming temperature, it is difficult to construct porous scaffolds of PA66/nanohydroxyapatite (PA66/HAp) by fused deposition modeling (FDM) three-dimensional (3D) printing. In this study, we demonstrated for the first time a method for 3D printing PA66/HAp composites at room temperature, prepared PA66/HAp printing ink using a mixed solvent of formic acid/dichloromethane (FA/DCM), and constructed a series of composite scaffolds with varying HAp content. This printing system can print composite materials with a high HAp content of 60 wt %, which is close to the mineral content in natural bone. The physicochemical evaluation presented that the hydroxyapatite was uniformly distributed within the PA66 matrix, and the PA66/HAp composite scaffold with 30 wt % HAp content exhibited optimal mechanical properties and printability. The results of in vitro cell culture experiments indicated that the incorporation of HAp into the PA66 matrix significantly improved the cell adhesion, proliferation, and osteogenic differentiation of bone marrow stromal cells (BMSCs) cultured on the scaffold. In vivo animal experiments suggested that the PA66/HAp composite material with 30 wt % HAp content had the best structural maintenance and osteogenic performance. The three-dimensional PA66/HAp composite scaffold prepared by low temperature printing in the current study holds great potential for the repair of large-area bone defects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.