Abstract
In the present work alkaline iron oxide nanoparticles are synthesized by a novel solvo thermal approach and characterized exhaustively by various complementary techniques. Field emission scanning electron microscopy (FESEM) studies reveal that the size of nanoparticles is in the range of 31.5 nm to 96.9 nm. Energy-dispersive X-ray spectroscopy spectral analysis reveals the presence of oxygen, carbon, iron, and sodium. The X-ray diffraction studies confirm the formation of tetragonal NaFeO2 as the major phase along with orthorhombic NaFeO2·H2O and rhombohedral FeCO3 (siderite) as the minor phases. Fourier transform infrared spectroscopy exhibits peaks due to the stretching and bending vibrations of O-H, C=O, CH3-N, CH3, C-H, C-N, and Fe-O groups. Differential scanning calorimetry (DSC) results display an endothermic peak at 100.85°C and a very small endothermic peak at 791.56°C with 819.73 mJ and 349.28 mJ energies respectively. These DSC peaks can be correlated with thermal gravimetric analysis (TGA) peaks representing 31.04% weight loss and 7.70% weight loss respectively in the sample at around 160°C and 980°C respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.