Abstract
A gel polymer electrolyte based on the blend of poly(methyl methacrylate-co-acrylonitrile-co-lithium methacrylate) (PMAML) and poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) was prepared and characterized. The synthesized PMAML were characterized by FTIR and 1 H NMR, respectively, and the surface morphology of the PMAML and PVDF-HFP blend membrane was also observed by scanning electron microscope (SEM). The electrochemical properties of composite electrolyte membranes were studied. The ionic conductivity of the polymer electrolyte composed of 75 wt.% 1 M LiBF 4 in ethylene carbonate (EC) and dimethyl carbonate (DMC) (EC:DMC=1:1 by weight) was about 2.6×10 −3 S cm −1 at ambient temperature. The electrochemical window of the polymer electrolyte was about 4.6 V determined from the linear sweep voltammetry plot. The lithium ion polymer batteries were assembled by sandwiching gel polymer electrolyte between LiCoO 2 cathode and mesophase carbon fibre (MPCF) anode. Charge–discharge test results display that lithium ion batteries with these gel polymer electrolytes have good electrochemical performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.