Abstract
Abstract A potassium nitrate–lithium nitrate–sodium nitrate (KNO3-LiNO3-NaNO3) eutectic mixture having a low melting point has been proposed as an alternative high-temperature quench medium. Inconel and steel probes were used to compare the quench performance of a conventional sodium nitrite (NaNO2) eutectic mixture and the proposed alternative medium at different bath temperatures. For the Inconel probe, the heat extraction rate was higher in the eutectic LiNO3 mixture maintained at 150°C. At elevated bath temperatures of 200°C, 250°C, and 300°C, the heat extraction rate was higher in the eutectic NaNO2 mixture. AISI 52100 steel probes quenched in eutectic LiNO3 quench medium at 150°C and 200°C showed higher hardness. At bath temperatures of 250°C and 300°C, the hardness of AISI 4140 steel probes quenched in both media was comparable. Wettability studies on Inconel and steel surfaces revealed the occurrence of nonuniform dilation of a LiNO3 eutectic mixture droplet. On the steel surface, the phenomenon occurred at lower temperatures, which resulted in an extended boiling stage and increased hardness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.