Abstract
Ir–Zr gradient coating was obtained on the Mo substrate by double glow plasma. The structure and composition of the coatings were confirmed by SEM, AFM, XRD and EDS, respectively. The adhesion strength between the coating and the substrate was evaluated by a scratch tester. Compared with preferential growth orientation of (220) crystal plane of Ir coating, the Ir–Zr coating had a random orientation structure. The RMS roughness value of the Ir–Zr coating is 19.3nm, which was lower than the roughness value of 45nm for Ir coating. The Ir–Zr coating with the thickness of 5.0μm was composed of two distinct layers. The proportion of Ir decreased gradually from the surface of the coating to the coating/substrate interface. The Zr distribution decreased slightly in the coating. The adhesive force of the Ir–Zr coating was 15N.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.