Abstract
A novel system Li2Mg3Ti1-x(Al1/2Nb1/2)xO6-4wt%LiF(0.02 ≤ x ≤ 0.08) ceramics were synthesized by the solid stated reaction method to improve the microwave dielectric properties of the ceramics. The phase composition, sintering characteristics and microwave dielectric properties of Li2Mg3Ti1-x(Al1/2Nb1/2)xO6-4wt%LiF(0.02 ≤ x ≤ 0.08) ceramics were then explored. The results demonstrated that at the optimal sintering temperature(900 °C), with the (Al1/2Nb1/2)4+ ions increased, the εr value decreased and the absolute value of τƒ augmented. Moreover, the Q × f value of ceramics was in accord with the relative density, which enlarged at first until the doping content reached the solid solubility limit (0.04 mol) of the ceramics. In total, the Li2Mg3Ti1-0.96(Al1/2Nb1/2)0.04O6-4wt%LiF ceramics sintered at 900 °C for 6 h showed the best microwave dielectric properties of εr~15.54, Q × f~154,000 GHz and τƒ~-38.3 ppm/°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.