Abstract
Considering the high thermal conductivity of copper material and the promoting effect of sulfonate ions on methane hydrate formation, in this study, copper nanowires coated with sulfonate polymer (CuNW@PSS) were used in methane hydrate experiments. The morphology of synthesized CuNW@PSS was confirmed by SEM and TEM, and the composition was analyzed by elemental analysis, it has clearly core–shell structure. The surface wettability of the material changed from hydrophilic to hydrophobic after sulfonate modification. In methane hydrate formation experiments, compared with PSS, CuNW@PSS can shorten the induction time by 78.5 %, from 61.87 ± 21.71 min to 13.28 ± 5.47 min, the growth rate increased by 130 %, from 0.6 ± 0.13 mmol/min to 1.38 ± 0.34 mmol/min. In addition, CuNW@PSS has good cycling and defoaming performance in the multi-cycle methane hydrate formation and dissociation experiments, which would have potential application for natural gas storage and transportation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.