Abstract

To extend the service life of the agitator blade, a series of [Cr–Fe4Co4Ni4]Cr2.6−x Ti x Mo0.4 (x = 0, 0.3, 0.6, and 0.9) high‐entropy alloy (HEA) compositions based on the cluster‐plus‐glue‐atom model is designed, and HEA coatings are deposited on 904L stainless steel using the laser cladding technique. The phase structure, microhardness, wear resistance, corrosion resistance, and erosion properties of the HEA coatings are determined using X‐ray diffractometer, transmission electron microscope, a microhardness tester, a friction and wear tester, an electrochemical workstation, and an erosion testing machine, respectively. The coating's phase structure is made of FCC solid solution. The coatings’ microhardness, wear, corrosion, and erosion resistance gradually improve by adding Ti. In particular, the microhardness of the [Cr–Fe4Co4Ni4]Cr1.7Ti0.9Mo0.4 coating reaches a peak value of 295.11 HV0.2, over 1.5 times that of the 904L stainless steel (190 HV0.2). Its specific wear rate (3.64 mm3 N−1 m−1) is lower than that of the substrate (8.53 mm3 N−1 m−1). The impedance of the [Cr–Fe4Co4Ni4]Cr1.7Ti0.9Mo0.4 coating is roughly 5.3 times of the 904L stainless steel. Simultaneously, the coating's cumulative volume loss rate of erosion–corrosion (0.054 mm3 h−1) is lower than that of the substrate (0.063 mm3 h−1). Consequently, the innovative HEA coating has an impressive overall performance.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.