Abstract
Abstract Zinc borate having the formula of 4ZnO·B2O3·H2O has been used as a fire retardant for polymers requiring high processing temperatures since it has a high dehydration temperature (around 415°C). The effects of reaction time, reaction temperature were investigated on the heterogeneous reaction between solid zinc oxide and boric acid solution. A stoichiometric amount of zinc oxide and 5.0% excess boric acid were used in experiments and the other parameters, mixing speed (1700 rpm), the solid-liquid ratio of 20%, and the amount of seed crystal (3.9% wt) were kept constant for all experiments. A 91.1% conversion was obtained at 120°C for 5 h of reaction time. Precipitated product was filtered and washed by hot water to remove the excess boric acid. Finally it was dried until reaching to a constant mass in an air circulating oven at 105°C. Powder products were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). FTIR spectrum and XRD pattern of powders are consistent with data of the zinc borate given in the literature. According to SEM analysis, whiskers are less than 1 μm in diameter and their lengths are in the range of 1–10 μm.
Highlights
Zinc borate having the formula of 4ZnO⋅B2O3⋅H2O has been used as a fire retardant for polymers requiring high processing temperatures since it has a high dehydration temperature
As zinc oxide is insoluble in the aqueous phase, the reaction of boric acid and zinc oxide is a heterogeneous even though a portion of ZnO dissolves in the acidic medium of boric acid solution
Boric acid is a Lewis acid producing proton by dissolving in water where zinc oxide particles are attacked by those protons
Summary
Abstract: Zinc borate having the formula of 4ZnO⋅B2O3⋅H2O has been used as a fire retardant for polymers requiring high processing temperatures since it has a high dehydration temperature (around 415°C). The effects of reaction time, reaction temperature were investigated on the heterogeneous reaction between solid zinc oxide and boric acid solution. A stoichiometric amount of zinc oxide and 5.0% excess boric acid were used in experiments and the other parameters, mixing speed (1700 rpm), the solid-liquid ratio of 20%, and the amount of seed crystal (3.9% wt) were kept constant for all experiments. Precipitated product was filtered and washed by hot water to remove the excess boric acid. Powder products were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). FTIR spectrum and XRD pattern of powders are consistent with data of the zinc borate given in the literature. According to SEM analysis, whiskers are less than 1 μm in diameter and their lengths are in the range of 1-10 μm
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.