Abstract
ABSTRACTIn this paper, fabrication and characterisation of Mg–SiC nanocomposite are investigated. Micrometre-sized Mg powder with the different volume fraction of SiC nano particles were dynamically compacted using a modified Split Hopkinson Pressure Bar. Moreover, the compaction process was simulated using AUTODYN commercial software to demonstrate that the stress in the powder sample was sufficient for consolidation. To achieve the best quality samples, the effects of lubrication and compaction velocity on dynamic compaction process were initially studied by experiment. It was observed that the temperature of 450°C and the compaction velocity of 15.5 m/s led to the best samples with relative density more than 99%. The effects of reinforcing phase content on the relative density, micro-hardness, and compressive behaviour of the compacted samples along with their microstructures were investigated. The results showed that the micro-hardness and the compressive strength of the samples fabricated at 450°C increased about 70% and 50%, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.