Abstract
High-efficiency solar cells require printed metal contacts with adapted emitters to ensure high fill factors. Multi-crystalline silicon (mc-Si) substrates require adapting the temperature ramps of rapid thermal processing (RTP) to avoid minority carrier lifetime degradation from activated defect centers. Sufficient temperature difference is required between front and back surfaces during co-firing to prevent junction leakage on the front and proper aluminum back surface field (Al-BSF) on the back surface. Actual temperature profile for co-firing in RTP after screen printing is a key issue for high-quality metal–semiconductor contact for high efficiency solar cell. A novel approach for optimization of co-firing temperature profile in RTP is investigated by measuring the actual temperature of front and back surfaces of the solar cell. Rapid cooling in the spike firing profile is made possible by controlling the gas flow rate in the RTP chamber during co-firing. For the best front and back metal contact and enhancement of minority carrier lifetime, the actual temperature of the silver (Ag)-printed surface is 605 °C and that of Al-printed surface is 743 °C. Mc-Si solar cell with fill factor (FF) 0.79 and conversion efficiency 15.02% is fabricated using the optimized co-firing temperature of RTP in a conventional solar cell production line.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.