Abstract
Black phosphorene-waterborne polyurethane (BPWPU) composite polymer with 0.2 wt % of black phosphorene was synthesized. Scanning electron microscopy (SEM) was used to observe the morphology of phosphorene in polyurethane matrix, which indicated that the phosphorene distributes uniformly in the PU matrix. The flammability measurements were carried out to investigate the flame-resistant performances of phosphorene, which indicated that phosphorene could effectively restrict the degradation of the PU membrane. Compared by the pure WPU, the limiting oxygen index (LOI) of BPWPU increased by 2.6%, the heat flow determined by thermal analysis significantly decreased by 34.7% moreover, the peak heat release rate (PHRR) decreased by 10.3%.
Highlights
A Novel Application of Phosphorene as aXinlin Ren 1,2 , Yi Mei 1,2, * ID , Peichao Lian 1,2, *, Delong Xie 1,2 , Yunyan Yang 1,2 , Yongzhao Wang 1,2 and Zirui Wang 1,2
Monolayer or several-layer black phosphorus (BP), named black phosphorene or phosphorene, is a type of two-dimensional (2D) nanomaterial with distinct physical/chemical properties due to the dimensionality effect
For further testifying the structure, X-ray diffraction (XRD) was carried out on the BP powders, as shown in Figure 2b, which indicated that the BP had a good crystallinity without
Summary
Xinlin Ren 1,2 , Yi Mei 1,2, * ID , Peichao Lian 1,2, *, Delong Xie 1,2 , Yunyan Yang 1,2 , Yongzhao Wang 1,2 and Zirui Wang 1,2. The Higher Educational Key Laboratory for Phosphorus Chemical Engineering of Yunnan Province, Kunming University of Science and Technology, Kunming 650500, Yunnan, China. Received: 19 January 2018; Accepted: 23 February 2018; Published: 26 February 2018
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.