Abstract
1000 MPa grade low-carbon martensite press hardening steels (PHS) are widely used in energy-absorbing domains of automotive parts, such as the bottom of a B-pillar. To prevent oxide scale formation during hot forming, this PHS is often required to be protected by an additional Al-Si coating. In addition, although the low carbon martensitic microstructure grants it excellent bending toughness, the ductility tends to be limited. In this study, a novel 1000 MPa grade ultrafine-grained (UFG) martensite-ferrite (F-M) dual-phase (DP) PHS with superior oxidation resistance was designed using tailored additions of Cr, Mn, and Si, and refining the initial microstructure. Only 0.55 ± 0.18 μm thick oxide film is formed in the designed steel during austenitizing heating and stamping, which is significantly lower than the 24.6 ± 3.1 μm thick oxide film formed in conventional 1000 MPa grade low-carbon martensite PHS under the identical condition. The superior oxidation resistance of designed steel can be attributed to the rapid formation of the protective Si-rich, Cr-rich, and Mn-rich oxide layers during annealing. Moreover, due to the presence of ferrite and ultrafine microstructure, the designed steel also shows a significant improvement in ductility from 8.5% to 16.8% without sacrificing strength and bending toughness compared with conventional 1000 MPa grade low-carbon martensite PHS.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.