Abstract
Enhancing the tribological characteristics of polyamide 6 (PA6) represents an effective strategy for extending the service life of self-lubricating PA6 composites. In this investigation, hollow mesoporous carbon spheres (HMCs) with an average diameter of 10 μm were synthesized using the template method, and the crucial factors influencing HMCs preparation were thoroughly examined. Successful synthesis of polyalphaolefin oil-containing microcapsules (PAO40@HMCs) was achieved, utilizing HMCs as microcontainers and PAO40 lubricant as the core material. The self-lubricating PAO40@HMCs microcapsules exhibited a notable oil content of 76.0 wt%. The tribological properties of the prepared self-lubricating PA6 composites were significantly better than those of pure PA6. When the content of PAO40@HMCs microcapsules in the composite reached 7 wt%, the coefficient of friction (COF) for the PA6 composite decreased by 87.9% (from 0.420 to 0.051), and the wear loss was reduced by 80% (from 0.115 to 0.023 g/0.5h). Through an analysis of the morphology and transfer film of the wear surface and friction pair, it was evident that microcapsules played a pivotal role in enhancing the self-lubricating properties of PA6 composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.