Abstract
Abstract A new pretreatment method has been developed to improve the catalytic activity of the Ni-Fe-Mo-Co alloy electrode for hydrogen evolution reaction (HER). The procedure involves pre-electrolyzing the Ni-Fe-Mo-Co alloy electrode in 30% KOH solution containing 10% potassium sodium tartrate at 70°C for 2 h, until some of the Mo and Fe elements are leached out. The surface morphology of the Ni-Fe-Mo-Co alloy demonstrates a unique hive-like structure after the pretreatment, which has the pore size in a nanometer range (about 50 nm), a very large real surface area, and good stability. The results of the electrochemical studies show that compared to other similar electrode materials and the treated Ni-Fe-Mo-Co electrode by leaching method, the pre-treated Ni-Fe-Mo-Co electrode has a much lower overpotential and much higher exchange current density for HER. In addition, a long-term continuous electrolysis test with a current interruption shows that the Ni-Fe-Mo-Co alloy has excellent catalytic stability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.