Abstract
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method has been validated by cyclic bending metallic glass and tungsten microcantilevers. The experiments reveal a stable crack growth during the lifetime of both samples. The metallic glass shows less plasticity due to the absence of dislocations, but shows shearing caused by the deformation. The crack growth rates determined in the tests follow Paris’ power law relationship. The results are reliable, reproducible and comparable with macroscopic setups. Due to the flexibility of the method, it is suitable for the characterization of specific microstructural features, like single phases, grain boundaries or different grain orientations.Graphical abstract
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.