Abstract
The paper uncovers an underlined mechanism of joining Yttrium Iron Garnet (YIG) and Magnesium Titanate Ceramic (MTC) with a bismuth-based glass braze. The proposed joint design has not been investigated until present. The central hypothesis is as follows. The brazed bismuth-based glass microstructure and the resulting mechanical strength of a YIG/MTC joint design support favorably a good bonding of the interface domains. The supporting evidence includes the following: (i) the bismuth-based glass features good wettability on YIG and MTC, (ii) the sequence of the coefficients of thermal expansions (YIG, bismuth-based glass, MTC) is in a favorable succession. The study reveals that the interface reactions form: (i) a lamellar phase and YBO3 whiskers at the YIG/Bi25 interface, (ii) both MgFe2O4, and Bi4Ti3O12 whiskers in addition to Zn2Ti3O8 reaction layer at the MTC/Bi25 interface, and (iii) Fe2O3 phase along the brazing seam. The mechanical integrity of joints has been studied as well.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.