Abstract
The layered LiNi0.40Mn0.40Co0.20O2 compound was synthesized and modified with a mixed alumina–carbon coating by a simple soft chemical route. The simultaneous presence of alumina and carbon on the surface of coated samples was proved by ICP-AES, chemical analysis, XP spectroscopy, SEM microanalysis and local electron diffraction. For the first time, we show that the alumina epitaxial layer is formed on basal {001} facets of cathode grains, whereas side-view facets, like {010}, remain free from crystalline α-Al2O3, thus leaving them easy for Li-ion diffusion into cathode structure. An amorphous carbon film was used here for better conductivity of the coating layer and prevention of the electrical contact loss between cathode grains. Electrochemical tests revealed that the mixed alumina-carbon coating applied on LiNi0.40Mn0.40Co0.20O2 stabilizes the surface structure and improves the cycling performance (3–4.5 V) and rate capability of cathodes on their basis compared with the pristine and alumina-coated LiNi0.40Mn0.40Co0.20O2 samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.