Abstract
The hydration kinetics of tricalcium silicate (C3S), the main constituent of portland cement, were analyzed with a mathematical “boundary nucleation” model in which nucleation of the hydration product occurs only on internal boundaries corresponding to the C3S particle surfaces. This model more closely approximates the C3S hydration process than does the widely used Avrami nucleation and growth model. In particular, the boundary model accounts for the important effect of the C3S powder surface area on the hydration kinetics. Both models were applied to isothermal calorimetry data from hydrating C3S pastes in the temperature range of 10°–40°C. The boundary nucleation model provides a better fit to the early hydration rate peak than does the Avrami model, despite having one less varying parameter. The nucleation rate (per unit area) and the linear growth rate of the hydration product were calculated from the fitted values of the rate constants and the independently measured powder surface area. The growth rate follows a simple Arrhenius temperature dependence with a constant activation energy of 31.2 kJ/mol, while the activation energy associated with the nucleation rate increases with increasing temperature. The start of the nucleation and growth process coincides with the time of initial mixing, indicating that the initial slow reaction period known as the “induction period” is not a separate chemical process as has often been hypothesized.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.