Abstract
To lower the operating temperatures of solid oxide fuel cells (SOFCs), A new A-site-deficient Ti-doped SrCoO3-δ (SCT) are synthesized by a modified Pechini method and used as new highly active and stable cathode materials for intermediate-temperature SOFCs. The phase structure and electrical, thermal, and electrochemical properties of the SCT samples are evaluated. A phase transformation of SrCoO3-δ from hexagonal to cubic perovskite structure occurred at room temperature by the substitution of Ti. A lower TEC value of the SCT oxide was observed with increasing the Ti doped content and A-site deficiency. NiO-SDC-supported single cells with various SCT as cathode materials were operated at intermediate temperatures using humidified H2 as fuel and the static air as oxidant, respectively. Significant improved electrochemical performance for the A-site-deficient SCT sample was observed. An open-circuit potential of 0.83 V and the max power density of 745 mW cm-2 were achieved at 650 °C. The experimental results indicated that the A-site-deficient Sr0.95Co0.9Ti0.1O3-δ cubic perovskites are promising candidates as cathode materials for IT-SOFCs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.