Abstract
Nanoindentation tests were carried out to investigate certain elastic properties of Al 2O 3/SiC p composites at microscopic scales (nm up to μm) and under ultra-low loads from 3 mN to 250 mN, with special attention paid to effects caused by SiC particles and pores. The measured Young’s modulus depends on the volume fraction of SiC particles and on the composite porosity and it can compare with that of alumina. The Young’s modulus exhibits large scatters at small penetrations, but it tends to be constant with lesser dispersion as the indentation depth increases. Further analysis indicated that the scatter results from specific microstructural heterogeneities. The measured Young’s moduli are in agreement with predictions, provided the actual role of the microstructure is taken into account.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.