Abstract
AbstractDespite of the good stability with Li‐metal, Li6.75La3Zr1.75Ta0.25O12(LLZTO) suffers from large interfacial resistance and severe Li‐metal penetration. Herein, a dual layer ceramic electrolyte of Ti‐doped LLZTO(Ti‐LLZTO)/LLZTO was developed, with the reducible Ti‐LLZTO layer contacting Li‐metal and the LLZTO layer contacting cathode. The identical crystal structures of Ti‐LLZTO and LLZTO enables a seamless contact and a barrierless Li+ transport between them. The densities of Ti‐LLZTO pellets are higher than that of LLZTO. With an in situ reduction of Ti‐LLZTO by Li‐metal, the interfacial wettability was improved and a mixed ion‐electron conducting layer was created. Both features help to reduce defects/pores on interface and homogenize the interfacial ionic/electronic flux, facilitating the reduction of interfacial resistance and suppression of dendrites. With the help of Ti‐LLZTO layer, long‐term stable lithium plating/stripping was reached in an areal capacity of 3.0 mAh cm−2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.