Abstract
Ribbons of Fe100−xGax (x=15, 17.5, 19.5 and 22.5) were prepared by rapid solidification from the melt. 57Fe Mössbauer spectroscopy and high resolution neutron diffraction have revealed that Fe100−xGax alloys with x=15 and 17.5 have the disordered bcc (A2) structure even after annealing, but the alloy with x=19.5 developed the short-range ordered D03 phase when annealed. The x=22.5 alloys showed mainly D03 phase with a fraction of bcc phase. A fraction of the bcc phase transformed into D03 phase and the long-range ordering of D03 phase was improved after annealing. 57Fe Mössbauer spectra showed no observable L12 phase in any samples even though less than 1% volume of L12 phases has been found in the annealed samples by neutron diffraction. The additional absorption at hyperfine field of 25T in x=22.5 samples was regarded as a result of imperfect D03 structure, rather than L12 phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.