Abstract
AbstractTo combine good chemical stability and high oxygen permeability, a mixed ionic‐electronic conducting (MIEC) 75 wt % Ce0.85Gd0.1Cu0.05O2−δ‐25 wt % La0.6Ca0.4FeO3−δ (CGCO‐LCF) dual‐phase membrane based on a MIEC–MIEC composite has been developed. Copper doping into Ce0.9Gd0.1O2−δ (CGO) oxide enhances both ionic and electronic conductivity, which then leads to a change from ionic conduction to mixed conduction at elevated temperatures. For the first time we demonstrate that an intergranular film with 2–10 nm thickness containing Ce, Ca, Gd, La, and Fe has been formed between the CGCO grains in the CGCO‐LCF one‐pot dual‐phase membrane. A high oxygen permeation flux of 0.70 mL min−1 cm−2 is obtained by the CGCO‐LCF one‐pot dual‐phase membrane with 0.5 mm thickness at 950 °C using pure CO2 as the sweep gas, and the membrane shows excellent stability in the presence of CO2 even at lower temperatures (800 °C) during long‐term operation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.