A microscopic investigation of failure mechanisms in a triaxially braided polyimide composite at room and elevated temperatures

Abstract

An experimental investigation is conducted on a unique triaxially braided polyimide composite material in order to track the development of microscopic damage leading to failure. Tensile static and fatigue tests are conducted at both room and elevated temperatures. Edge replication and scanning electron microscopy are employed to track damage development and to identify failure mechanisms, respectively. Static tests reveal that although the elevated temperature environment does not significantly alter the mechanical properties of the composite, its influence on the development of microscopic damage development is notable. The dominant damage mechanism of braider yarn cracking is mitigated at elevated temperatures as a direct result of resin softening, which is also the case for the fatigue test specimens. The result of the temperature-dependent microscopic damage development is a reduction in the fatigue lives at elevated temperatures. This study yielded an improved understanding of microscopic damage mechanisms and local deformation behavior for an advanced composite material, which is valuable for designers.