Abstract
The design and production of Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn-based dipole and quadrupole magnets is critical for the realization of the High-Luminosity Large Hadron Collider (HL-LHC) at the European Organization for Nuclear Research (CERN). Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn superconducting coils are aimed at enhancing the bending and focusing strengths of accelerator magnets for HL-LHC and beyond. Due to the brittle nature of Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn, the coil fabrication steps are very challenging and require very careful QA/QC. Flaws in the Nb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> Sn filaments may lead to quenches, and eventually, performance limitation below nominal during magnet testing. A novel inspection method, including advanced non-destructive and destructive techniques, was developed to explore the root-causes of quenches occurring in performance-limiting coils. The most relevant results obtained for MQXF coils through this innovative inspection method are presented. This approach allows for precise assessment of the physical events associated with the quenches experienced by magnet coils, mainly occurring in the form of damaged strands with transversely broken sub-elements. Coil-slice preparation, micro-optical observations of transverse and longitudinal cross-sections, and a deep etching technique of copper will be illustrated in the present work, with a focus on the results achieved for a CERN coil from a non-conforming quadrupole magnet prototype, and two coils fabricated in the US, in the framework of the Accelerator Upgrade Project (AUP) collaboration, from two different non-conforming quadrupole magnets, respectively. The results obtained through the proposed inspection method will be illustrated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.