Abstract
Pyroelectric coefficient measurements were made at various temperatures for poled and unpoled samples of PVDF films. Samples were produced using the spin-coating technique onto glass substrates. Experiments were made using the quasi-static technique. PVDF samples were poled at various electric field strengths and the relation between poling field strength and the pyroelectric coefficient was investigated. The effect of the poling temperature was also studied. The maximum pyroelectric coefficient was obtained for a poling temperature of 340 K and for a poling field strength of \( 14MVm^{ - 1} \). Dielectric permitivity and dielectric loss measurements were also performed in the 125–375 K temperature range.