Abstract
This work addresses the applicability of a local criterion incorporating the coupling of critical stress and a critical hydrogen concentration to predict hydrogen embrittlement effects on the fracture strength of high strength steels using notched round specimens with different notch root radii. The numerical simulations incorporating a relatively simple hydrogen transport model provide strong support for the adoption of a failure criterion in terms of achieving a critical level of tensile stress coupled to the local hydrogen concentration, which, in turn, enable the construction of a failure locus for the degraded material. For the cases analyzed here, construction of such a failure locus based on a critical combination of maximum principal stress and hydrogen concentration enabled predictions of fracture strength for hydrogen-charged tensile specimens which are in very good agreement with experimental data. Overall, the results presented here lend additional support for further developments of a local stress-based criterion to predict hydrogen embrittlement effects on the fracture strength of high strength steels.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.