Abstract
AbstractThe functional lithiophilic−lithiophobic gradient solid electrolyte interphase (SEI) between Li‐metal anode and solid‐state polymer electrolytes may be effective in addressing the long‐standing issue of side reactions and Li‐dendrite growth during repeated deposition or dissolution in solid‐state polymer‐based high‐energy‐density batteries. Herein, a reliable lithiophilic–lithiophobic gradient SEI (G‐SEI) of LiAg‐LiF/Li3N is in situ formed by AgTFSI, used as an additive for polyethylene oxide‐based electrolyte (PEO‐Ag). The upper layer consists of a lithiophobic LiF/Li3N‐rich layer, wherein LiF possesses a high interfacial energy, while Li3N enables fast Li+ diffusion, which synergistically facilitates the uniform deposition of Li+. Lithiophilic Li–Ag alloy can effectively reduce the nucleation overpotential and promote more planar growth of lithium. Furthermore, such G‐SEI possesses a high mechanical modulus, mitigating the penetration of dendrites through the SEI and thereby preventing the continuous degradation of the PEO‐based electrolyte. As a result, an over three times improvement in the lifespan of Li | PEO‐Ag | LFP cell is achieved, demonstrating an 81.4% capacity retention rate after 500 cycles at 1C, as compared to Li | PEO | LFP cell with common SEI. Thus, the developments of the lithiophilic‐lithiophobic gradient SEI provide a substantial path toward high‐performance solid‐state lithium batteries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.