Abstract
The durability and reliability of thermal barrier coatings(TBCs) have become a major concern of hot-section components due to lack of a reliable life prediction model. In this paper, it is found that the failure location of TBCs is at the TBC/TGO interface by a sequence of crack propagation and coalescence process. The critical crack length of failure samples is 8.8mm. The crack propagation rate is 3-10µm/cycle at the beginning and increases largely to 40µm/cycle near coating failure. A life prediction model based a simple fracture mechanics approach is proposed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.