Abstract
This work reports the results of laboratory experiments conduced to follow the kinetics of strontium recovery into the Al–Mg alloy by metallothermic reduction of SrO. The reagent was incorporated to molten alloy by the use of submerged powders injection technique. The variables analyzed were the injection time, the melt temperature and the initial magnesium content. Magnesium is added to the melt to increase the reactivity and reduce the surface tension of the molten aluminum. It was possible to increase the strontium content from 0 to 5 wt.% after 60 min of treatment. The results were fitted to a general kinetic equation, which allowed it to obtain the kinetic parameters, i.e. order of reaction and activation energy of the process. As the main mechanism of the strontium recovery process is of diffusive type, the global process rate increases as the temperature and initial amount of the magnesium increased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.